Browsing by Author "Cintura, Eleonora"
Now showing 1 - 3 of 3
Results Per Page
Sort Options
- Agro-industrial wastes as building insulation materials : A review and challenges for Euro-Mediterranean countriesPublication . Cintura, Eleonora; Nunes, Lina; Esteves, Bruno M.; Faria, PaulinaThis study investigates the possibility of using agro-industrial wastes for building products, mainly focusing on their insulation properties. A classification of bio-wastes is provided, namely of the lignocellulosic ones and their features and properties are described. Information about three main topics is collected: world production and consumption of some crops already used as building materials, their chemical composition and their most studied properties. Since the considered materials are lignocellulosic and they have many common features, a comparison is made. The aim is to have comparable information to support future research related to the production of eco-efficient indoor insulation boards. The result of this research is the choice of four different agro-industrial wastes produced in the Euro-Mediterranean Countries. This area was chosen as buildings typically have little or no insulation due to the regional mild climate; however, particularly with climate change, indoor hygrothermal comfort is poor. The collection of information allows some conclusions to be reached about the different bio-wastes already studied and identify gaps in the literature.
- Cement-Bonded Particleboards with Banana Pseudostem Waste : Physical Performance and Bio-SusceptibilityPublication . Nunes, Lina; Cintura, Eleonora; Parracha, João Luís; Fernandes, Bruno; Silva, Vitor; Faria, PaulinaThis article evaluates the relevant properties of cement-bonded particleboards (CBPB) made with a portion of maritime pine (Pinus pinaster) particles replaced with an agricultural waste, banana pseudostem (Musa sp.). The industrial production of CBPB was simulated in the laboratory based on a reference composition defined by a manufacturing company. Test specimens were produced assuming 0%, 25%, 50% and 75% partial replacement of wood particles with banana pseudostem fibres. Some physical properties (bulk density, thermal conductivity, and dimensional stability) and the mould susceptibility of the different variables were assessed. Results show that the thermal conductivity of the boards increased with the banana fibre proportion and ranged between 0.233 W/(m.K) and 0.279 W/(m.K). The bulk density values generally increased with the banana fibre proportion and ranged between 1754–1995 kg/m3, being the highest value obtained for B50 (equal weight proportion of wood particles and banana fibres). Specimens with a higher percentage of banana fibres have reduced thickness resulting from swelling, ranging between 0.38% and 0.11% (for 0% and 75% of banana fibres, respectively). CBPBs with unsanded surfaces seem to be unsusceptible to mould development, whereas those with sanded surfaces, simulating wearing, show some bio-susceptibility. Mould development increases with the proportion of banana fibre. The results highlight the need for regular maintenance of the particleboards, thus avoiding surface wear over time and resulting in the exposure of the wood particles and/or banana fibres to the outside environment.
- Characterization of an Arundo donax-based composite: A solution to improve indoor comfortPublication . Cintura, Eleonora; Faria, Paulina; Molari, Luisa; Barbaresi, Luca; D'ORAZIO, DARIO; Nunes, LinaABSTRACT: Arundo donax (giant reed or giant cane) is a widely available, perennial, invasive, non-food crop, present worldwide and employed for several uses, including building practices. Considering the increasing demand for sustainable building materials, A. donax can be an efficient solution. This study investigated its properties as a bio-aggregate mixed with a sodium silicate solution as an adhesive. A horizontal analysis that provided a general characterization of the composite was carried out. The results showed that the A. donax-based composite had an apparent density of 517 kg/m³, thermal conductivity of 0.128 W/(m.K), and high hygroscopicity, with a moisture buffering value of 4.33 g/(m² %RH), property that could be both an advantage for indoor comfort and a drawback. The uncommon sound absorption behaviour can be comparable to granular materials, with the highest sound absorption coefficient values, α, between 600 Hz and 700 Hz. Due to the range and the shape of the acoustic absorption property, this material may be helpful in acoustic treatments for speech noise. The mechanical tests defined flexural and compressive strength, respectively, 0.35 N/mm² and 0.9 N/mm², ensuring applicability. Above all, these tests opened new possible solutions for A. donax-based composite production either alone or in combination with other agro-industrial wastes and justified further tests, such as fire resistance and bio-susceptibility.